Polyvinyl Chloride sheets and rods,is a flame retardant,chemical stability,low rifting forces produced
only a non-crystalline materials,is the most widely used plastic materials.While its material properties
including high strength,high stiffness and high hardness,operating temperature range from minus 15
degrees to 60 degrees,bonding,can be welded.
Dimensions:
PVC Sheet:(1-100mm)1000*2000mm PVC Rod:φ(10-250mm)1000mm
| PVC Sheet | ||
| T. (mm) | W. (mm) | L. (mm) |
| 2 | 1000*2000 | 6.2 |
| 2.5 | 1000*2000 | 7.75 |
| 3 | 1000*2000 | 9.3 |
| 4 | 1000*2000 | 12.4 |
| 5 | 1000*2000 | 15.5 |
| 6 | 1000*2000 | 18.6 |
| 7 | 1000*2000 | 21.7 |
| 8 | 1000*2000 | 24.8 |
| 10 | 1000*2000 | 31 |
| 12 | 1000*2000 | 37.2 |
| 15 | 1000*2000 | 46.5 |
| 16 | 1000*2000 | 49.6 |
| 18 | 1000*2000 | 55.8 |
| 20 | 1000*2000 | 62 |
| 22 | 1000*2000 | 68.2 |
| 25 | 1000*2000 | 77.5 |
| 30 | 1000*2000 | 93 |
| 35 | 1000*2000 | 108.5 |
| 40 | 1000*2000 | 124 |
| 50 | 1000*2000 | 155 |
| 60 | 1000*2000 | 186 |
| 70 | 1000*2000 | 217 |
| 80 | 1000*2000 | 248 |
| 100 | 1000*2000 | 310 |
| PVC Rod | ||
| Dia. (mm) | L. (mm) | Kgs/pc |
| 20 | 1000 | 0.50 |
| 25 | 1000 | 0.79 |
| 30 | 1000 | 1.13 |
| 35 | 1000 | 1.54 |
| 40 | 1000 | 2.01 |
| 45 | 1000 | 2.54 |
| 50 | 1000 | 3.14 |
| 55 | 1000 | 3.80 |
| 60 | 1000 | 4.52 |
| 65 | 1000 | 5.31 |
| 70 | 1000 | 6.16 |
| 75 | 1000 | 7.07 |
| 80 | 1000 | 8.04 |
| 85 | 1000 | 9.08 |
| 90 | 1000 | 10.18 |
| 100 | 1000 | 12.57 |
| 110 | 1000 | 15.20 |
| 120 | 1000 | 18.10 |
| 130 | 1000 | 21.24 |
| 140 | 1000 | 24.63 |
| 150 | 1000 | 28.27 |
| 160 | 1000 | 32.17 |
| 180 | 1000 | 40.71 |
| 200 | 1000 | 50.26 |
PVC Product
PVC Properties
| ITEM | METHOD | UNIT | PVC |
| Autai Mechanical Properties | |||
| Long Term Working Temp | ℃ | 60 | |
| Density | ASTM D792 | g/cm3 | 1.35 |
| Yield stretch strength | ASTM D638 | Mpa | 50 |
| Breaking stretch strength | ASTM D638 | Mpa | |
| Breaking strength rate | ASTM D638 | % | 10 |
| Bending modulus | ASTM 790 | Mpa | 2400 |
| Hardness shore | Shore D | Mpa | 108 |
| Impact strength | ASTM D256 | KJ/M2 | 50 |
| Thermal Properties | |||
| Melting point | DSC | ℃ | 120 |
| Heat distortion temperature | ASTM D648 | ℃ | 70 |
| Maximum operating temperature | ℃ | ||
| Thermal conductivity | DIN 52612-1 | W/(K -M) | |
| Coefficient of linear expansion | ASTM D696 | 10-5-1/K | 80x10-6 |
| ElectricalProperties | |||
| Dielectric constant | ASTM D150 | - | |
| Dielectric loss coefficient | ASTM D150 | - | |
| Volume resistivity | ASTM D257 | Q.cm | 1015 |
| Surface resistivity | ASTM D257 | Q | 1016 |
| Dielectric strength | ASTM D149 | KV mm | 30 |
| Chemical Properties | |||
| Equilibrium water content | 23℃ 60%RH | % | 0.2 |
| Acid resistance | 23℃ 60%RH | + | |
| Alkali resistance | 23℃ 60%RH | + | |
| Acid and alkali water resistance | 23℃ 60%RH | + | |
| Chlorine,Acid,Alkali resistance | 23℃ 60%RH | 0 | |
| Aromatic compound resistance | 23℃ 60%RH | 0 | |
| Ketone resistance | 23℃ 60%RH | - | |
| Hot water resistance | 23℃ 60%RH | + | |
| Others | |||
| Combustibility | UL 94 | V-0 | |
| Adhesion | + | ||
| Non toxic harmless sexual | EEC 90/128 FDA | - | |
| Friction coefficient | DIN 53375 | 0.6 | |
| Uitraviolet UV resistance | |||
Remarks:
1.“+"means anti,"-"means none;"O"means "it depends on reality testing conditions.
2.Above data are provided by the raw material
3.Above data can not be regarded as the additional term for the contract.
4.These products we mentioned are not suitable for medicine and tooth transplantation.
Copyright © Jiangsu Vichen Composite Material Co., Ltd. All Rights Reserved. | Sitemap | Technical Support: