Nylon Rods

The Polyamides,commonly referred to as nylon and available in Sheet,Rod,Tube and Parts.The most common engineering

nylons are PA6,PA66,Oil Nylon.Nylon stock shapes are produced by either extrusion or casting.The process is in

part a determinant of the nylon properties of the end product.

Inquire Now Next Product

Product Details:

Nylon Rod
Dia. (mm)	L. (mm)	Kgs/pc
10	1000	0.11
15	1000	0.24
20	1000	0.42
25	1000	0.66
30	1000	0.95
35	1000	1.30
40	1000	1.70
45	1000	2.15
50	1000	2.65
55	1000	3.21
60	1000	3.82
65	1000	4.48
70	1000	5.20
75	1000	5.96
80	1000	6.79
85	1000	7.66
90	1000	8.59
100	1000	10.60
110	1000	12.83
120	1000	15.27
130	1000	17.92
140	1000	20.78
150	1000	23.86
160	1000	27.14
180	1000	34.35
200	1000	42.41

Nylon Product

Nylon Sheet
T. (mm)	W. (mm)	L. (mm)
6	1000*2000	16.2
7	1000*2000	18.9
8	1000*2000	21.6
10	1000*2000	27
12	1000*2000	32.4
15	1000*2000	40.5
20	1000*2000	54
25	1000*2000	67.5
30	1000*2000	81
35	1000*2000	94.5
40	1000*2000	108
45	1000*2000	121.5
50	1000*2000	135
55	1000*2000	148.5
60	1000*2000	162
65	1000*2000	175.5
70	1000*2000	189
80	1000*2000	216
90	1000*2000	243
100	1000*2000	270
120	1000*2000	324
130	1000*2000	351
150	1000*2000	405
160	1000*2000	432
180	1000*2000	486
200	1000*2000	540

Remark:

1.Tolerance s according to Thickness,Length and Width:0 to+5%

2.It is theoretical value for above spec with the 1000x2000mm or 1000mm,Taking objective as standard,isted data are for reference only 3.In stock products dimension:1000×2000mm,1200×2400mm:1000mm,2000mm:other need customize.

4.The products above have been strictly treated with tempering,the strain value has met the minimum.

Nylon Product

Extruded Nylon6 Properties

ITEM	METHOD	UNIT	VALUE
Mechanical Properties
Specific gravity	ASTM D792	g/cm3	1.13
Tensile yield strength	ASTM D638	Mpa	74
Breaking elongation	ASTM D638	%	5
Bending strength	ASTM 790	Mpa	90
Flexural modulus	ASTM 790	Mpa	2200
Shore hardness	ASTM D2240	D	85
Impact strength	ASTM D256	J/M	50
Thermal Properties
Melting point	DSC	℃	220
Heat distortion temperature	ASTM D648	℃	70
Operating temperature	-	℃	85
Maximum operating temperature	-	℃	160
Thermal conductivity	DIN 52612 -1	W/(K -M)	0.23
Coefficient of linear thermal expansion	ASTM D696	10-5-1/K	8
Electrical Properties
Dielectric strength	ASTM D150	KV mm	25
Dielectric loss factor	ASTM D150	-	0.032
Volume resistivity	ASTM D257	Q.cm	1014
Surface resistivity	ASTM D257	Ω	1016
Dielectric constant	ASTM D149	-	4.2
Chemical Properties
Water absorption	23℃ 60%RH	%	1.28
Acid resistance	23℃60%RH		-
Alkali resistance			+
Acid and alkali resistance			+
Resistance to sodium chlorate			0
Resistance toaromatic compounds			+
Resistance to ketone	23℃ 60%RH		+
Resistance to hot water	23℃ 60%RH		+
Others
Flammability	UL 94		HB
Viscosity			+
Non toxic	EEC 90/128 FDA		+
Coefficient of friction	DIN 53375		0.36
Anti -ultraviolet

Remarks:

1.“+”:positive“-”:negative “0”:depends.

2.All Autai Nylon 6 the parameters above are based on raw material but not finished products,

MC Nylon Product

MCNylon Properties

ITEM	METHOD	UNIT	VALUE
Mechanical Properties
Tensile yield strength	GB/T 1040	Mpa	75-85
Modulus of elongation	ISO 527	Mpa	4100
Breaking elongation	ISO 527	%	>25
Max.compressive strength	ISO 604	Mpa	90-100
Coefficient of compressibility	ISO 604	Mpa	2700
Bending strength	ISO 178	Mpa	100-110
Elasticity bending modulus	ISO 178	Mpa	3300
Impact strength	ISO 180	KJ/M 2	5.4
Shore hardness	GB 3398	Shora D	83-85
Thermal Properties
Melting point	ISO 1218	℃	220
Max.intermit operating temperature		℃	180
Max.continuous operating temperature	-	℃	115
Min.intermit operating temperature	-	℃	-100
Min.continuous operating temperature	-	℃	-40
Coefficient of linear thermal expansion	ISO 11359	10-5-1/K	5-8
Electrical Properties
Dielectric constant	IEC 250	-	3.7
Dielectric strength	IEC 243	KV mm	>25
Volume resistivity	IEC 93	Ω.cm	10 15
Surface resistivity	IEC 93	Ω	10 15
Impedance	IEC 112	-	CTI600
Others
Specific gravity	USO 1183	g/cm³	1.15
abrasive resistance	-	-	0.41
Coefficient of friction	-	-	0.39